Alterations in damage processes in dense cancellous bone following gamma-radiation sterilization. Read more about Alterations in damage processes in dense cancellous bone following gamma-radiation sterilization.
Reassessment of computerized wear measurement for total hip arthroplasty with correction for projectional image distortion: a brief follow-up report. Read more about Reassessment of computerized wear measurement for total hip arthroplasty with correction for projectional image distortion: a brief follow-up report.
Reasons for revision of first-generation highly cross-linked polyethylenes. Read more about Reasons for revision of first-generation highly cross-linked polyethylenes.
Post damage in contemporary posterior-stabilized tibial inserts: influence of implant design and clinical relevance. Read more about Post damage in contemporary posterior-stabilized tibial inserts: influence of implant design and clinical relevance.
Near-terminal creep damage does not substantially influence fatigue life under physiological loading. Read more about Near-terminal creep damage does not substantially influence fatigue life under physiological loading.
In vivo oxidation contributes to delamination but not pitting in polyethylene components for total knee arthroplasty. Read more about In vivo oxidation contributes to delamination but not pitting in polyethylene components for total knee arthroplasty.
Do first-generation highly crosslinked polyethylenes oxidize in vivo? Read more about Do first-generation highly crosslinked polyethylenes oxidize in vivo?
Crack propagation resistance is similar under static and cyclic loading in crosslinked UHMWPE: a pilot study. Read more about Crack propagation resistance is similar under static and cyclic loading in crosslinked UHMWPE: a pilot study.
Crack initiation in retrieved cross-linked highly cross-linked ultrahigh-molecular-weight polyethylene acetabular liners: an investigation of 9 cases. Read more about Crack initiation in retrieved cross-linked highly cross-linked ultrahigh-molecular-weight polyethylene acetabular liners: an investigation of 9 cases.